Statement of problem
Studies that evaluate the survival rate and load to fracture of premolars restored with inlays produced using different methods are lacking.
The purpose of this in vitro study was to compare the survival rate and fracture load of premolars restored with inlays fabricated using different methods.
Material and methods
Thirty maxillary premolars were selected, embedded, and prepared to receive inlays fabricated using different methods (n=10): LaCom-digital scanning with Lava C.O.S. scanner (3M ESPE), followed by milling of composite resin block (Lava Ultimate; 3M ESPE) in a milling unit; CeCom-digital scanning with Cerec 3D Bluecam scanner (Dentsply Sirona), followed by milling of a Lava Ultimate block in Cerec (Dentsply Sirona); PresDis-impression with polyvinyl siloxane, inlay made using the lost wax technique, and IPS e.max Press (Ivoclar Vivadent AG) pressed ceramic (lithium disilicate). A dual-polymerizing resin cement system was used to lute the inlays. Inlays were mechanically cycled (2 Hz, 106 mechanical pulses, 80 N) after 24 hours, and the specimens were stored in distilled water at 37°C for 11 months. Then, a fatigue test was conducted using a 10-Hz frequency and 400-N load on the inner inclines of the cusps. The test was complete when the specimen fractured or when the specimen reached 1.5×106 cycles. The specimens that survived fatigue testing were submitted to a single-load fracture test in a universal testing machine and analyzed using a stereoscope for failure classification. Survival rates were estimated using the Kaplan-Meier method and log-rank test (Mantel-Cox). Fracture load data were analyzed using 1-way ANOVA (α=.05).
No significant differences were detected among the groups for the survival rate (P=.87) or for the load to fracture (P=.78). Most failures were longitudinal, catastrophic fractures.
Premolars restored with inlays fabricated using the tested methods had similar survival rates and loads to fracture.
To read this article in full you will need to make a payment
Purchase one-time access:Academic & Personal: 24 hour online accessCorporate R&D Professionals: 24 hour online access
One-time access price info
- For academic or personal research use, select 'Academic and Personal'
- For corporate R&D use, select 'Corporate R&D Professionals'
Subscribe:Subscribe to Journal of Prosthetic Dentistry
Already a print subscriber? Claim online access
Already an online subscriber? Sign in
Register: Create an account
Institutional Access: Sign in to ScienceDirect
- Effect of in vivo crown margin discrepancies on periodontal health.J Prosthet Dent. 1991; 65: 357-364
- Micro-computed tomography evaluation of marginal fit of lithium disilicate crowns fabricated by using chairside CAD/CAM systems or the heat-pressing technique.J Prosthet Dent. 2014; 112: 1134-1140
- Clinical evaluation of all-ceramic crowns fabricated from intraoral digital impressions based on the principle of active wavefront sampling.J Dent. 2010; 38: 553-559
- Full arch scans: conventional versus digital impressions-an in-vitro study.Int J Comput Dent. 2011; 14: 11-21
- Different methods for inlay production: effect on internal and marginal adaptation, adjustment time, and contact point.Oper Dent. 2017; 42: 436-444
- An evaluation of student and clinician perception of digital and conventional implant impressions.J Prosthet Dent. 2013; 110: 420-423
- Current state of development and perspectives of machine-based production methods for dental restorations.Int J Comput Dent. 1999; 2: 9-35
- Effect of restorative procedures and occlusal loading on cuspal deflection.Oper Dent. 2006; 31: 33-38
- The effect of mechanical loading on the cusp defection of premolars restored with direct and indirect techniques.J Contemp Dent Pract. 2014; 15: 75-81
- Stress fatigue: Basic principles and prosthodontic implications.Int J Prosthodont. 1995; 8: 105-116
- Indirect posterior composite resins.Compend Contin Educ Dent. 2005; 26: 495-503
- Wear evaluation of MZ100 compared to ceramic CAD/CAM materials.Int J Comput Dent. 2001; 4: 171-184
- Minimal preparation designs for single posterior indirect prostheses with the use of the Cerec system.Inter J Comput Dent. 2008; 11: 227-240
- Tensile bond strength of resin composite repair in vitro using different surface preparation conditionings to an aged CAD/CAM resin nanoceramic.Clin Oral Investig. 2014; 19: 299-308
- Elastic properties of lithium disilicate versus feldspathic inlays: effect on the bonding by 3D finite element analysis.J Prosthodont. 2018; 27: 741-747
- Ceramic inlays: effect of mechanical cycling and ceramic type on restoration-dentin bond strength.Oper Dent. 2016; 41: 102-117
- Effects of cement thickness and bonding on the failure loads of CAD/CAM ceramic crowns: multi-physics FEA modeling and monotonic testing.Dent Mater. 2012; 28: e99-e109
- A comparison of fatigue resistance of three material for cusp-replacing adhesive restorations.J Dent. 2006; 34: 19-25
Published online: August 07, 2018
© 2018 by the Editorial Council for The Journal of Prosthetic Dentistry.