Effects of the rare earth element lanthanum on the metal-ceramic bond strength of dental casting Co-Cr alloys

      Abstract

      Statement of problem

      The metal-ceramic bond strength of dental casting Co-Cr alloys may be improved by the addition of the rare earth element lanthanum (La), but studies are lacking.

      Purpose

      The purpose of this in vitro study was to evaluate the effects of the rare earth element La on the metal-ceramic bond strength of dental casting Co-Cr alloys.

      Material and methods

      Four groups of specimens with different La content (0; 0.02 wt%; 0.04 wt%; 0.06 wt%) were prepared using conventional casting methods. The metal-ceramic bond strength was assessed by using the 3-point bend test. The microstructures were characterized by metallurgical microscopy, scanning electron microscopy, and X-ray diffraction analyses. The morphology and element distribution of metal-ceramic interfaces were evaluated by scanning electron microscopy coupled with energy-dispersive X-ray spectroscopy. The results of bond strengths were statistically analyzed by the Tukey honest significant difference (HSD) test (α=.05).

      Results

      The specimens showed typical dendritic microstructures, few defects, and island-shaped intermetallic compounds rich in Mo and Cr, mainly consisting of α-Co phase of a face-centered cubic (FCC) structure and ε-Co phase of a close-packed hexagonal (HCP) structure. As the amount of La increased, the thickness of the native oxide layer and the diffusion layer at the interface increased, and the wettability between the oxide layer and the metal matrix improved. The mean ±standard deviation values of the metal-ceramic bond strengths were 28.11 ±4.53 MPa for group 0%, 33.13 ±5.65 MPa for group 0.02%, 37.48 ±7.86 MPa for group 0.04%, and 40.70 ±5.17 MPa for group 0.06%. The statistical analysis indicated that significant differences (P<.05) were observed among all groups tested, except for group 0.04% and 0.06% (P>.05). The debonded surfaces of Co-Cr specimens showed a mixed type of adhesive and cohesive fractures.

      Conclusions

      The microstructures, morphologies, and compositions of oxide films were influenced by the La content, and the La addition could significantly improve the metal-ceramic bond strength of dental casting Co-Cr alloys.
      To read this article in full you will need to make a payment

      Purchase one-time access:

      Academic & Personal: 24 hour online accessCorporate R&D Professionals: 24 hour online access
      One-time access price info
      • For academic or personal research use, select 'Academic and Personal'
      • For corporate R&D use, select 'Corporate R&D Professionals'

      Subscribe:

      Subscribe to Journal of Prosthetic Dentistry
      Already a print subscriber? Claim online access
      Already an online subscriber? Sign in
      Institutional Access: Sign in to ScienceDirect

      References

        • Mrázová M.
        • Klouźková A.
        Leucite porcelain fused to metals for dental restoration.
        Ceram-Silik. 2009; 53: 225-230
        • Akova T.
        • Ucar Y.
        • Tukay A.
        • Balkaya M.C.
        • Brantley W.A.
        Comparison of the bond strength of laser-sintered and cast base metal dental alloys to porcelain.
        Dent Mater. 2008; 24: 1400-1404
        • Ucar Y.
        • Akova T.
        • Akyil M.S.
        • Brantley W.A.
        Internal fit evaluation of crowns prepared using a new dental crown fabrication technique: laser-sintered Co-Cr crowns.
        J Prosthet Dent. 2009; 102: 253-259
        • Li J.
        • Chen C.
        • Liao J.
        • Liu L.
        • Ye X.
        • Lin S.
        • et al.
        Bond strengths of porcelain to cobalt-chromium alloys made by casting, milling, and selective laser melting.
        J Prosthet Dent. 2017; 118: 69-75
        • Rosenstiel S.F.
        • Land M.F.
        • Fujimoto J.
        Contemporary fixed prosthodontics.
        5th ed. Mosby, St. Louis2016: 538-540
        • O'Connor R.P.
        • Mackert Jr., J.R.
        • Myers M.L.
        • Parry E.E.
        Castability, opaque masking, and porcelain bonding of 17 porcelain-fused-to-metal alloys.
        J Prosthet Dent. 1996; 75: 367-374
        • Uusalo E.K.
        • Lassila V.P.
        • Yli-Urpo A.U.
        Bonding of dental porcelain to ceramic-metal alloys.
        J Prosthet Dent. 1987; 57: 26-29
        • Anusavice K.J.
        Phillips' science of dental materials.
        12th ed. W.B. Saunders, Philadelphia2012: 621-654
        • Yilmaz H.
        • Dincer C.
        Comparison of the bond compatibility of titanium and an NiCr alloy to dental porcelain.
        J Dent. 1999; 27: 215-222
        • Jabbari Y.S.A.
        • Koutsoukis T.
        • Barmpagadaki X.
        • Zinelis S.
        Metallurgical and interfacial characterization of PFM Co-Cr dental alloys fabricated via casting, milling or selective laser melting.
        Dent Mater. 2014; 30: 79-88
        • Vasquez V.Z.
        • Ozcan M.
        • Kimpara E.T.
        Evaluation of interface characterization and adhesion of glass ceramics to commercially pure titanium and gold alloy after thermal- and mechanical-loading.
        Dent Mater. 2009; 25: 221-231
        • Lu Y.
        • Chen W.
        • Ke W.
        • Wu S.
        Nickel-based (Ni-Cr and Ni-Cr-Be) alloys used in dental restorations may be a potential cause for immune-mediated hypersensitivity.
        Med Hypotheses. 2009; 73: 716-717
        • Bagby M.
        • Marshall S.J.
        • Marshall Jr., G.W.
        Metal ceramic compatibility: a review of the literature.
        J Prosthet Dent. 1990; 63: 21-25
        • Xiang N.
        • Xin X.Z.
        • Chen J.
        • Wei B.
        Metal-ceramic bond strength of Co-Cr alloy fabricated by selective laser melting.
        J Dent. 2012; 40: 453-457
        • Wu C.M.L.
        • Yu D.Q.
        • Law C.M.T.
        • Wang L.
        Properties of lead-free solder alloys with rare earth element additions.
        Mat Sci Eng R. 2004; 44: 1-44
        • Ferro R.
        • Saccone A.
        • Borzone G.
        Rare earth metals in light alloys.
        J Rare Earth. 1997; 15: 45-50
        • Yu S.
        • He Z.
        • Meng C.
        • Chen K.
        Effects of cerium on the mechanical properties of the ZA22/Al2O3 composites.
        J Rare Earth. 1995; 13: 27-30
        • Pieraggi B.
        • Rapp R.A.
        • Hirth J.P.
        Role of interface structure and interfacial defects in oxide scale growth.
        Oxid Met. 1995; 44: 63-79
        • Karaali A.
        • Mirouh K.
        • Hamamda S.
        • Guiraldenq P.
        Effect of tungsten 0–8 wt.% on the oxidation of Co–Cr alloys.
        Comp Mater Sci. 2005; 33: 37-43
        • Weiss G.B.
        Cellular pharmacology of Lanthanum.
        Annu Rev Pharmacol. 1974; 14: 343-354
        • International Organization for Standardization
        ISO 9693-1(E). Dentistry – Compatibility testing – Part 1: metal-ceramic systems.
        ISO, Geneva2012 (Available at:)
        • Xin X.Z.
        • Xiang N.
        • Chen J.
        • Wei B.
        In vitro biocompatibility of Co-Cr alloys fabricated selective laser melting or traditional casting techniques.
        Mater Lett. 2012; 88: 101-103
        • Knap F.J.
        • Ryge G.
        Study of bond strength of dental porcelain fused to metal.
        J Dent Res. 1966; 45: 1047-1051
        • Anusavice K.J.
        • Horner J.A.
        • Fairhurst C.W.
        Adherence controlling elements in ceramic-metal systems. I. Precious alloys.
        J Dent Res. 1977; 56: 1045-1052
        • Sakaguchi R.L.
        • Powers J.M.
        Craig's restorative dental materials.
        13th ed. Mosby-Year Book Inc, St. Louis2012: 231-251
        • Xu C.L.
        • Wang H.Y.
        • Yang Y.F.
        • Wang H.Y.
        • Jiang Q.C.
        Effect of La2O3 in the Al-P-Ti-TiC-La2O3 modifier on primary silicon in hypereutectic Al-Si alloys.
        J Alloy Compd. 2006; 421: 128-134
        • Christensen R.J.
        • Tolpygo V.K.
        • Clarke D.R.
        The influence of the reactive element yttrium on the stress in alumina scales formed by oxidation.
        Acta Mater. 1997; 45: 1761-1766
        • Shao N.
        • Dai J.W.
        • Li G.Y.
        • Nakae H.
        • Hane T.
        Effect of La on the wettability of Al2O3 by molten aluminum.
        Mater Lett. 2004; 58: 2041-2044
        • Xia Z.
        • Chen Z.
        • Shi Y.
        • Mu N.
        • Sun N.
        Effect of rare earth element additions on the microstructure and mechanical properties of Sn-Ag-Bi solder.
        J Electron Mater. 2002; 31: 564-567