Adhesion of veneering porcelain to cobalt-chromium dental alloys processed with casting, milling, and additive manufacturing methods: A systematic review and meta-analysis

      Abstract

      Statement of problem

      Selective laser melting (SLM) additive manufacturing (AM) technologies provide an alternative to conventional casting and milling procedures in fabricating metal-ceramic dental prostheses. However, the quality of porcelain bond strength to the SLM AM cobalt-chromium (Co-Cr) metal framework of a dental restoration is unclear.

      Purpose

      The purpose of this systematic review and meta-analysis was to identify in vitro studies that reported the porcelain bond strength to SLM AM Co-Cr dental metal alloys and compare the porcelain bond strength values to cast, milled, and additively manufactured Co-Cr dental alloys.

      Material and methods

      An electronic systematic review was performed in different databases: MEDLINE/PubMed, EMBASE, World of Science, Cochrane, and Scopus. A manual search was also conducted. Studies that reported the porcelain bond strength to SLM Co-Cr metal alloys and in the English language were included. Two investigators evaluated the quality assessment of the studies by applying the JBI critical appraisal checklist for quasi-experimental studies (nonrandomized experimental studies). A third investigator was consulted to resolve lack of consensus. Two subgroups were created based on the test used, 3-point bend and shear bond strength tests. The porcelain bond strength of cast, milled, and AM Co-Cr dental alloys were compared. The I2 statistic and its associated P value were used to assess the heterogeneity between studies. The Eger test was used for determining significance of the funnel pots.

      Results

      A total of 216 studies were collected from the electronic and manual searches. After independently evaluating the titles and abstracts by the reviewers, 26 articles were identified. Three of these were excluded after full-text revision. The porcelain bond strength comparison between the cast and AM alloys for the 3-point bend subgroup revealed a significant result for overall effect (P<.001) favoring the SLM method with considerable heterogeneity (I2=83%, P<.001). Furthermore, the porcelain bond strength comparison between cast and milled alloys for the shear bond strength subgroup revealed a significant test for overall effect (P=.04) favoring milled procedures with a nonsignificant unimportant heterogeneity (I2= 0%, P<.47) and for the 3-point bend subgroup (P<.001) favoring milled specimens with a significant considerable heterogeneity (I2=79%, P<.001).

      Conclusions

      The metal manufacturing method had no effect on the porcelain bond strength to Co-Cr dental metal alloys.
      To read this article in full you will need to make a payment

      Purchase one-time access:

      Academic & Personal: 24 hour online accessCorporate R&D Professionals: 24 hour online access
      One-time access price info
      • For academic or personal research use, select 'Academic and Personal'
      • For corporate R&D use, select 'Corporate R&D Professionals'

      Subscribe:

      Subscribe to Journal of Prosthetic Dentistry
      Already a print subscriber? Claim online access
      Already an online subscriber? Sign in
      Institutional Access: Sign in to ScienceDirect

      References

        • Anusavice K.J.
        • Hojjatie B.
        • Dehoff P.H.
        Influence of metal thickness on stress distribution in metal-ceramic crowns.
        J Dent Res. 1986; 9: 1173-1178
        • Scurria M.S.
        • Bader J.M.
        • Shugars D.A.
        Meta-analysis of fixed partial denture survival: Prostheses and abutments.
        J Prosthet Dent. 1998; 79: 459-464
        • Tan K.
        • Pjetursson B.E.
        • Lang N.P.
        • Chan E.S.Y.
        A systematic review of the survival and complication rates of fixed dental dentures (FDP) after an observation period of at least 5 years. III. Conventional FDPs.
        Clin Oral Impl Res. 2004; 15: 654-666
        • Pjetursson B.E.
        A systematic review of the survival and complication rates of all-ceramic and metal–ceramic reconstructions after an observation period of at least 3 years. Part I: single crowns.
        Clin Oral Implants Res. 2008; 3: 326-328
        • Brägger U.
        • Hirt-Steiner S.
        • Schnell N.
        • Schmidlin K.
        • Salvi G.E.
        • Pjetursson B.
        • et al.
        Complications and failures rates of fixed dental prostheses on patients treated for periodontal disease.
        Clin Oral Impl Res. 2011; 22: 70-77
        • Naylor W.P.
        Introduction to metal-ceramic technology.
        3rd Edition. Quintessence, Chicago, Illinois2018: 118-137
        • Roberts H.W.
        • Berzins D.W.
        • Moore B.K.
        • Charlton D.G.
        Metal-ceramic alloys in dentistry: a review.
        J Prosthodont. 2009; 18: 188-194
        • Torabi K.
        • Farjood E.
        • Hamedani S.
        Rapid prototyping technologies and their applications in prosthodontics, a review of literature.
        J Dent Shiraz Univ Med Sci. 2015; 16: 1-9
        • Revilla-León M.
        • Meyer M.J.
        • Özcan M.
        Metal additive manufacturing technologies: literature review of current status and prosthodontic applications.
        Int J Comput Dent. 2019; 22: 55-67
        • International Organization for standardization
        Standard ISO/ASTM 52900:2015 [ASTM F2792]. Additive Manufacturing - general principles and terminology.
        (Available at:)
        • International Organization for standardization
        Standard ISO 17296-2:2015. Additive manufacturing - General principles - Part 2: Overview of process categories and feedstock.
        (Available at:)
        • Anestiev L.A.
        • Froyen L.
        Model of primary rearrangement processes at liquid phase sintering and selective laser sintering due to biparticle interactions.
        J Appl Phys. 1997; 86: 4008-4017
        • Deckard C.R.
        Method and apparatus for producing parts by selective sintering.
        1986 (Patent US 4863538-A)
        • Deckard C.
        • Beaman J.
        Process and control issues in selective laser sintering.
        ASME Prod Eng Div. 1988; 33: 191-197
        • Meiners W.
        • Wissenbach K.
        • Gasser A.
        Selective laser sintering at melting temperature.
        1996 (Patent DE 19649865)
        • Yamamoto N.
        • Sakai K.
        Electron beam melting method for metallic material.
        2002 (Patent US 6858059B2)
        • Malhotra M.L.
        • Maickel L.B.
        Shear bond strength in porcelain- metal restorations.
        J Prosthet Dent. 1980; 43: 397-400
        • Moher D.
        • Liberati A.
        • Tetzlaff J.
        • Altman D.G.
        The PRISMA Group. Preferred Reporting Items for Systematic Reviews and Meta-Analyses: The PRISMA Statement.
        PLoS Med. 2009; 6: e1000097
        • The Joanna Briggs Institute (JBI)
        Critical Appraisal Checklist for Quasi-Experimental Studies (non-randomized experimental studies).
        (Available at:)
        • Higgins J.P.
        • Thompson S.G.
        Quantifying heterogeneity in a meta-analysis.
        Stat Med. 2002; 21: 1539-1558
        • Egger M.
        • Smith G.D.
        • Schneider M.
        • Minder C.
        Bias in meta-analysis detected by a simple, graphical test.
        British Medical Journal. 1997; 315: 629-634
        • Xiang N.
        • Xin X.Z.
        • Chen J.
        • Wei B.
        Metal-ceramic bond strength of Co-Cr alloy fabricated by selective laser melting.
        J Dent. 2012; 40: 453-457
        • Stawarczyk B.
        • Eichberger M.
        • Hoffmann R.
        • Noack F.
        • Schweiger J.
        • Edelhoff E.
        • et al.
        A novel CAD/CAM base metal compared to conventional CoCrMo alloys: an in-vitro study of the long-term metal-ceramic bond strength.
        Oral Health Dent Manag. 2014; 13: 446-452
        • Wu L.
        • Zhu H.
        • Gai X.
        • Wang Y.
        Evaluation of the mechanical properties and porcelain bond strength of cobalt-chromium dental alloy fabricated by selective laser melting.
        J Prosthet Dent. 2014; 111: 51-55
        • Kul E.
        • Aladag L.I.
        • Duymus Z.Y.
        Comparison of the metal-ceramic bond after recasting and after laser sintering.
        J Prosthet Dent. 2015; 114: 109-113
        • Bae E.J.
        • Kim H.Y.
        • Kim W.C.
        • Kim J.H.
        In vitro evaluation of the bond strength between various ceramics and cobalt-chromium alloy fabricated by selective laser sintering.
        J Adv Prosthodont. 2015; 7: 312-316
        • Wang H.
        • Feng Q.
        • Li N.
        • Xu S.
        Evaluation of metal-ceramic bond characteristics of three dental Co-Cr alloys prepared with different fabrication techniques.
        J Prosthet Dent. 2016; 116: 916-923
        • Ren X.W.
        • Zeng L.
        • Wei Z.M.
        • Xin X.Z.
        • Wei B.
        Effects of multiple firings on metal-ceramic bond strength of Co-Cr alloy fabricated by selective laser melting.
        J Prosthet Dent. 2016; 115: 109-114
        • Li J.
        • Chen C.
        • Liao J.
        • Liu L.
        • Ye X.
        • Lin S.
        • et al.
        Bond strengths of porcelain to cobalt-chromium alloys made by casting, milling, and selective laser melting.
        J Prosthet Dent. 2017; 118: 69-75
        • Kaleli N.
        • Saraç D.
        Comparison of porcelain bond strength of different metal frameworks prepared by using conventional and recently introduced fabrication methods.
        J Prosthet Dent. 2017; 118: 76-82
        • Lawaf S.
        • Nasermostofi S.
        • Afradeh M.
        • Azizi A.
        Comparison of the bond strength of ceramics to Co-Cr alloys made by casting and selective laser melting.
        J Adv Prosthodont. 2017; 9: 52-56
        • Yan X.
        • Xu Y.X.
        • Wu Y.
        • Lin H.
        Effects of heat treatment on metal-ceramic combination of selective-laser-melted cobalt-chromium alloy.
        J Prosthet Dent. 2018; 120: 319.e1-319.e6
        • Ekren O.
        • Ozkomur A.
        • Ucar Y.
        Effect of layered manufacturing techniques, alloy powders, and layer thickness on metal-ceramic bond strength.
        J Prosthet Dent. 2018; 119: 481-487
        • Nageshraj R.
        • Rajagopal M.P.
        • Madapathy S.
        • Samuel P.
        • Ramabhadran N.
        • Mathew J.
        An in vitro comparative evaluation of shear bond strengths of veneering porcelain and different core materials.
        J Contemp Dent Pract. 2018; 19: 1437-1443
        • Dimitriadis K.
        • Spyropoulos K.
        • Papadopoulos T.
        Metal-ceramic bond strength between a feldspathic porcelain and a Co-Cr alloy fabricated with direct metal laser sintering technique.
        J Adv Prosthodont. 2018; 10: 25-31
        • Han X.
        • Sawada T.
        • Schille C.
        • Schweizer E.
        • Scheideler L.
        • Geis-Gerstorfer J.
        • et al.
        Comparative analysis of mechanical properties and metal-ceramic bond strength of Co-Cr dental alloy fabricated by different manufacturing processes.
        Materials (Basel). 2018; 11: 1801
        • Di Fiore A.
        • Savio G.
        • Stellini E.
        • Vigolo P.
        • Monaco C.
        • Meneghello R.
        Influence of ceramic firing on marginal gap accuracy and metal-ceramic bond strength of 3D-printed Co-Cr frameworks.
        J Prosthet Dent. 2020; 124: 75-80
        • Kaleli N.
        • Ural Ç.
        • Küçükekenci A.S.
        The effect of layer thickness on the porcelain bond strength of laser-sintered metal frameworks.
        J Prosthet Dent. 2019; 122: 76-81
        • Dimitriadis K.
        • Papadopoulos T.
        • Agathopoulos S.
        Effect of bonding agent on metal-ceramic bond strength between Co-Cr fabricated with selective laser melting and dental feldspathic porcelain.
        J Prosthodont. 2019; 28: 1029-1036
        • Yoldan E.E.
        • Türker N.
        • Büyükkaplan U.S.
        • Özarslan M.M.
        • Karalı R.
        • Deniz A.T.
        Evaluation of the bond strengths between dental porcelain and cobalt-chromium metal frameworks manufactured with different techniques after the thermal aging process.
        Scanning. 2020; 2020: 9315236
        • Akova T.
        • Uçar Y.
        • Tukay A.
        • Balkaya M.C.
        • Brantley W.A.
        Comparison of the bond strength of laser-sintered and cast base metal dental alloys to porcelain.
        Dent Mater. 2008; 24: 1400-1404
        • Prasad M.N.
        • Jyoti N.B.
        • Sabita R.M.
        Comparative evaluation of shear bond strength of porcelain fused to metal substructure fabricated using conventional and contemporary techniques: an in vitro study.
        Int J Med Res Health Sci. 2015; 4: 186-192
        • Serra-Prat J.
        • Cano-Batalla J.
        • Cabratosa-Termes J.
        • Figueras-Àlvarez O.
        Adhesion of dental porcelain to cast, milled, and laser-sintered cobalt-chromium alloys: shear bond strength and sensitivity to thermocycling.
        J Prosthet Dent. 2014; 112: 600-605
        • Tulga A.
        Effect of annealing procedure on the bonding of ceramic to cobalt-chromium alloys fabricated by rapid prototyping.
        J Prosthet Dent. 2018; 119: 643-649
        • Antanasova M.
        • Kocjan A.
        • Kovač J.
        • Žužek B.
        • Jevnikar P.
        Influence of thermo-mechanical cycling on porcelain bonding to cobalt-chromium and titanium dental alloys fabricated by casting, milling, and selective laser melting.
        J Prosthodont Res. 2018; 62: 184-194
        • International Organization for standardization
        Standard 9693:2019. Dentistry - Compatibility testing for metal-ceramic and ceramic-ceramic systems.
        (Available at:)
        • Braga R.R.
        • Meira J.B.
        • Boaro L.C.
        • Xavier T.A.
        Adhesion to tooth structure: a critical review of "macro" test methods.
        Dent Mater. 2010; 26 (e38-49)
        • Van Noort R.
        • Noroozi S.
        • Howard I.C.
        • Cardew G.
        A critique of bond strength measurements.
        J Dent. 1989; 17: 61-67